F-931's' is a flexible, cross linked, high performance, high strength, fast set water base coating. F-931's' provides excellent glass particle containment for all types, shapes and sizes of glass products and containers. It's very low V.O.C.'s, non-flammable and high solids content make it an Emission Control Coating System, eccs®, that can be air dried or heat cured to meet production demands. F- 931's' can be dipped or brushed, is available in clear as well as a variety of custom colors. F-931-S exhibits excellent chemical, impact, abrasion, tear strength, UV and block resistance and offers excellent heat/non-yellowing properties.

Typical applications include protecting/ containment of low temperature CFL/CFT bulbs, colored/decorating low temp CFL/CFT bulbs, all types of glass products and containers.
Unit of Measure

Technical Specs

Brands

 N/A Performix®

Solids Weight

 N/A 37 to 39 %

Temperature Use Range

 N/A 0 to 250 ºF

Shelf Life

 N/A 1+ years at 77 ºF unopened container

Finish

 N/A Semi-Gloss

Chemical Resistance

 N/A Petroleum: Excellent
Acid, Alkaline: Good
Alcohol, Ketone, Chlorinated Solvent: Limited

Tensile

 N/A 3,680 psi

Elongation

 N/A 825 %

Elongation Test Method

 N/A American Society for Testing and Materials (ASTM D-412)

Tensile Test Method

 N/A American Society for Testing and Materials (ASTM D-412)

Abrasion

 N/A Excellent

Permeability

 N/A Limited

Weatherability

 N/A Excellent 7-10 years

Weatherability Test Method

 N/A American Society for Testing and Materials (ASTM G-53)

Freeze Thaw Stability

 N/A Excellent

Tear Resistance Test Method

 N/A American Society for Testing and Materials (ASTM D-1004)

Tear Resistance

 N/A 0.70

Alternative Products

 N/A Contact Technical Service.

Note

N/A For Industrial Use Only.

We cannot anticipate all conditions under which this information and our products, or the products of other manufacturers in combination with our products, may be used. We accept no responsibility for results obtained by the applications of this information or the safety and suitability of our products, either alone or in combination with other product combination for their own purposes. Unless otherwise agreed in writing, we sell the products without warranty, and buyers and users assume all responsibility and liability for loss or damage arising from the handling and use of our products whether used alone or in combination with other products. Ever changing V.O.C. regulations in your area may require you to contact local authorities for proper use and/or disposal of this product. Should you need further assistance, please contact PLASTI DIP INTERNATIONAL technical service.

PLASTI DIP, HCF® eccs®, Performix and logo are registered trademarks of PLASTI DIP INTERNATIONAL
BINKS is a registered trademark of BINKS MFG. CO., Franklin Park, IL

Surface Preparations

N/A MIX WELL BEFORE USE.
All surfaces to be coated must be free of all oils, grease, dirt, wax, and mold release.

USE ADEQUATE VENTILATION.

Spraying

N/A Pressure pot/conventional sprayers may be used. Gently mix before spraying. Apply wet, overlapping coats, holding gun 6"-12" from surface, using a 4"- 6" pattern. Allow to completely dry before applying additional coats to desired thickness.

Recommended Equipment and Settings

N/A Gun: Binks® model 2100
Nozzle: 63B
Cap: 63PB or 66SD-3 for heavier build up
Needle: 663A
Material: 25 psi
Atomization: 15-25 psi
Dilution: None required
Clean up: Water, mild solvent if allowed to dry

Industrial/commercial airless equipment may be used. Use as described above.

Tip sizes: 0.011-0.019
Pressure: As needed
Dilution: As needed

Dipping

N/A Gently mix before each use. Do not introduce air bubbles. Insert item 1" every 5 seconds. Remove at same rate. Allow to completely dry before applying additional coats to desired thickness.

Hints

N/A For storage or dip tank containers, use only poly or galvanized steel. A dry film thickness of 2-3 mils is recommended for most applications. To speed drying, mild heat (95ºF-130ºF) and air flow may be used. To cross link bake coated product between 130-350ºF for upto 30 minutes. Do not stack or store parts in contact with each other if not fully cured. Avoid excessive air movement, heat or humidity. Always use proper ventilation and protection.

Brush/Roller

N/A Gently mix before each use. Apply wet overlapping coats using a foam brush, pad or roller. Allow to completely dry before applying additional coats to desired thickness.